Study on the Utilization of Barite in Making Carbon Film Ceramic Resistor

탄소피막 저항기용 자기소체 제조에 있어 Barite 활용에 관한 연구

  • Published : 1982.02.01

Abstract

Instead of barium carbonate, domestic barite was used as the flux in manufacturing theinsulating porcelain. To avoid the problems arising from the decomposition of barite in the body during firing, BaO.$Al_2O_3$ was synthesized at $1300^{\circ}C$ for 5 hours. synthetic BaO.$Al_2O_3$ was mixed with other materials such as kaoline, alumina, clay, dolomite. The RO content (CaO. MgO. BaO) of the batches was varied from range of 4 to 14wt. % at 2wt. % - intervals, and firing temperature was varied from 1280 to 140$0^{\circ}C$-at 4$0^{\circ}C$ intervals The properties such as water absorption, bulk density. mechnical strength, specific resistance, and linear shrinkage were measured. The body containing 12 wt.% of RO content showed the satisfactory for the application in the Fixed Carbon Film Resistor.

Keywords

References

  1. An Encyclopedia of the Ceramic Industries v.2 no.222 Jasper Ware A. B. Searle
  2. Korea Cermaic Industry Association v.3 no.1 Technical Information for Ceramic Industry
  3. 요업학회지 v.18 no.3(52) 알칼리토족 산화물이 물라이트 자기의 진기적 특성에 미치는 영향 주기태;장성도
  4. J. Am. Ceram. Soc. v.30 no.3 Alkaline Earth Porcelains possesing Low Dielectric Loss M. D. Rigerink;R. O. Grisdale
  5. J. Am. Ceram. Soc. v.2 no.7 Special Spark-Plug Porcelains A. V. Bleininger;F. H. Riddle
  6. Introduction to Glass Science L. D. Pye;H. J. Stcvcns;W. C. Lacourse
  7. Introduction to Ceramic W. D. Kingery;H. K. Bowen;Dr. Uhlmann
  8. Priciples of Solid State Chemistry(Reaction in Solid) P. P. Bundikv;A. M. Ginstling
  9. J. Am. Ceram. Soc. v.39 no.2 Barite in Ceramic White Ware Ralston Russel;J. R. Cmilo Valencia;H. W. Emrich