A Study on Durability of High Strength Concrete

고강도(高强度)콘크리트의 내구성(耐久性)에 관한 연구(研究)

Using superplasticizer or the methods of autoclave curing is the most typical and practical of the ways to make high strength concrete. In this study the high strength concrete piles by way of centrifugal forming and hand compacting, are put to the freezing and thawing test after the process of autoclave curing, water curing after steam curing, or stand water curing. And the relation of such piles to durability, the rate of strength decrease, and the rate of weight variation is shown. The durability of those test piles throughout freezing and thawing test proves to be comparatively sufficient in the above-mentioned curings when the piles contain a proper quantity of air. But it is also acknowledged that without A.E agent, the high strength concrete piles of autoclave curing is higher than those of the other curing in strength, but lower in modulus of dynamic elasticity and their durability factor after the test is much lower.

고강도(高强度)콘크리트의 제조방법중(製造方法中) 가장 대표적(代表的)이고 실용적(實用的)인 것으로 고성능감수제(高性能減水劑)와 고온고압양생(高溫高壓養生)에 의(依)한 방법등(方法等)이 있다. 본연구(本硏究)에서는 이와같은 고강도(高强度)콘크리트로 만든 콘크리트 Pile을 원심력성형(遠心力成形)과 손다짐으로 만들어 각각(各各)에 대(對)하여 Autoclave 양생(養生), Steam 양생후(養生後) 수중(水中) 14일(日) 양생(養生) 및 표준수중양생(標準水中養生)하여 동결융해시험(凍結融解試驗)을 하였으며 각종(各種)에 대(對)하여 내구성(耐久性)의 상관적(相關的)인 관계(關係)를 규명하였다. 이들 공시체(供試體)들의 동결융해(凍結融解)에 대(對)한 내구성(耐久性)은 일반적(一般的)으로 적당량(適當量)의 공기량(空氣量)을 함유(含有)하고 있을 때 상기(上記) 여러 가지 양생(養生)에 대(對)하여 비교적(比較的) 충분(充分)한 내구성(耐久性)이 있는 것으로 판명(判明)되었으나 AE제(劑)를 사용(使用)하지 않은 경우에는 Autoclave 양생(養生)한 고강도(高强度)콘크리트는 타양생(他養生)한 고강도(高强度)콘크리트보다 강도면(强度面)에서는 높았으나 동탄성계수(動彈性係數)가 좀 낮았고 시험후(試驗後)의 내구성계수(耐久性係數)도 극(極)히 약(弱)하였다. 그러나 원심력성형(遠心力成形)한 non AE 콘크리트 Pile은 표준양생(標準養生)하였을 때 내구성계수(耐久性係數)가 100 이상(以上)이었으며 중량감소(重量減少)도 없었다는 사실로 미루어 타 공시체보다 내구성(耐久性)이 우수함을 알 수 있었다.