Basic Studies on Propellant Casting (II). Effects of Solid Additives on Urethane Polymerization

추진제 성형에 관한 기초연구 (제2보). 우레탄 중합에 미치는 첨가제 효과

  • 전용구 (인하대학교 이과대학 화학과) ;
  • 이익춘 (인하대학교 이과대학 화학과) ;
  • 김시준 (한양대학교 자연과학대학 화학과)
  • Published : 1981.08.30
Download PDF
⟨ Previous Next ⟩

Abstract

Kinetic studies were carried out on urethane polymerization reaction of hydroxyl-terminated polybutadiene with isophorone diisocyanate under presence of Hexogen as solid additive. The rate was found to increase with the amount of Hexogen added. However the rate acceleration was not a catalytic effect but solely due to an increase of activation entropy. The reaction was a good 2nd order process with nearly constant activation energy of 8.4 kcal/mole.

Solid인 Hexogen 존재하에서 hydroxyl-terminated polybutadiene과 isophorone diisocyanate의 혼성중합반응속도에 관하여 연구하였다. 중합반응속도는 Hexogen의 첨가량이 증가할 수록 빠르게 나타났지만, Hexogen의 촉매적 역할은 없었으며, 오직 entropy control에 의한 반응임을 밝혔다. 이 반응은 2차 반응속도법칙에 잘 일치하며, activation energy는 8.4 Kcal/mole로 거의 일정하다.

Keywords

References

  1. Chemistry and Technology of Explosives v.I;II T. Urbanski
  2. Report UCRL-51319 Lawrence Livemore Laboratory Properties of Chemical Explosives and Explosive Simulants Brigitta M. Doberatz
  3. J. Appl. Ploym. Sci. v.20 R. Y. Yee;A. Adicoff
  4. J. Appl. Polym. Sci. v.24 T. J. Thomas;V. N. Krishnamurthy
  5. J. Appl. Polym. Sci. v.24 K. Kishore;V. R. Paiverneker;R. Vasanthakumari
  6. J. Chem. Soc. J. W. Baker;J. B. Holdsworth
  7. I. Lee;Y. K. Cheun;K. W. Cha
  8. Analyst v.71 H. E. Stagg
  9. J. Chem. Soc. J. W. Baker;J. Gaunt
  10. J. Chem. Soc. J. N. Greenshieds;R. H. Peters;R. F. T. Stepto
  11. Rate and Equilibria of Org. Reaction J. E. Leffler;E. Grunwald
  12. J. Amer. Chem. Soc. v.63 P. I. Rlory