A Study on the kinetics of Aluminizing of Cold rolled Steel Sheets

冷間壓廷鋼板의 Aluminizing에 對한 速度論的인 硏究

The Rates of formation and heats of activation for the intermatallic Compound Layers between Cold rolled sheet and molten aluminium &ath (adding small amounts of silicon) has been determined by Continous aluminizing method in the temperature range of 680$^{\circ}$ to 760$^{\circ}C$ and with immerssion time. The structure of the intermetallic Compound Layers was the shape of "Tongues" in pure Al-Bath and Al-Bath Containing 1% Si, But in Al-5% Si Bath was "Band" the Composition of the intermetallic Compound Layers were checked by microhardness measurements and X-Ray probe micro analyzer. FeAl intermetallic Compound layer was found to be uniform in pure Al-Bath and Al-5% Si Bath, But Fe Al intermetallic Compound Layer was shown in Al-1% Si Bath. The growth Rates of the intermetallic Compound Layers was most rapidly increased at Temperatures from 720$^{\circ}$ to 760$^{\circ}C$, at the immorsion time above 60 Second in pure Al-Bath, But in Al-1% Si Bath was solwly increased for the same conditions, and then in Al-5% Si Bath was hardly effected by these experimental condition. Heasts of activation of 29, 46 Kcal per mole which calculuted from Layer growth experiments were found in pure Al-Bath, Al-1% Si Bath respectively.