Studies on the Hardening of Briquette Ash

연탄재의 경화(硬化)에 관(關)한 연구(硏究)

Comparative studies have been carried out to elucidate effects of 3 types of Japanese hardening agents and cement on the compressive and tensil strength of solidified briquette ashes with different ages, when various mixing ratio were applied. 1. The hardening agent, especially type C, were appeared to be better than the cement to obtain higher compressive and tensil strength of the products. 2. The compressive strength when mixing ratio of 1 : 3 applied were : $177.6kg/cm^2$. for type C; $168.6kg/cm^2$ for type A; and $155.94kg/cm^2$ for type B. 3. The tensil strength when mixing ratio of 1 : 3 applied were: $24.63kg/cm^2$ for type C ; $23.14kg/cm^2$ for type B; and $22.45kg/cm^2$ for type A. 4. Although the solidified briquette ashes were found to be not as strong as cement mortar, it is (considered that they could be used instead of low-strength concrete, and that they could contribute to reduce the amount of terminal city-wastes then to reduce pollutions caused by the wastes.

연탄재의 경화(硬化)에 관한 연구(硏究)를 위하여 일본산(日本産) 경화재(硬化材) 3종(種)으로 연탄재를 경화시킨 경우와 국내산(國內産) 시멘트로 연탄재를 경화시킨 경우의 압축강도(壓縮强度)와 인장강도(引張强度)를 배합별(配合別), 재령별(材令別)로 구분(區分)하여 비교(比較) 시험(試驗)한 결과(結果)를 요약(要約)하면 다음과 같다. 1. 경화재(硬化材) 사용(使用)이 시멘트 사용(使用)모다 압축강도(壓縮强度) 인장강도(引張强度가 높으게 나타났으며 그 중에서도 C종(種)이 가장 높았다. 2. 압축강도(壓縮强度)는 1 : 3일 때 C종(種)에서 $177.6kg/cm^2$ A종(種)에서 $168.6kg/cm^2$ B종(種)에서 $155.94kg/cm^2$의 순(順)으로 나타났다. 3. 인장강도(引張强度)는 1 : 3일 때 C종(種)에서 $24.63kg/cm^2$ B종(種)에서 $23.14kg/cm^2$ A종(種)에서 $22.45kg/cm^2$의 순(順)으로 나타났다. 4. 시멘트 모르터에 비하면 저강도(低强度)이지만 저강도(低强度)의 콘크리트 제품(製品)에 이용(利用)이 가능(可能)하다고 보며 연탄재를 고형화(固形化)함으로써 폐기물(廢棄物)에 의한 공해방지(公害防止)와 폐기물(廢棄物) 처리(處理)의 노력(勞力) 절약(節約)과 최종처분(最終處分)의 폐기물(廢棄物)의 양(量)이 감량(減量)되고 폐기물(廢棄物)의 유효이용(有效利用)으로 자원(資源)의 절약(節約)에 유익(有益)하다고 사료(思料)된다.