$CS_2$ / KOH Catalysis에 의한 ${\varepsilon}$-Caprolactam의 음이온 중합 (제3보)

Anionic Polymerization of ${\varepsilon}$-Caprolactam via $CS_2$ / KOH Catalysis (Ⅲ)

  • 구명서 (한국과학원 화학 및 화학공학과) ;
  • 최삼권 (한국과학원 화학 및 화학공학과)
  • 발행 : 1977.12.30

초록

$CS_2$/KOH catalysis를 이용해서 ${\varepsilon}$-caprolactam의 음이온중합을 시키고 percent conversion과 점도를 측정하였다. $80^{\circ}C,\;105^{\circ}C$의 비교적 낮은 온도에서는 $CS_2$/KOH mole ratio가 0.5일때 percent conversion이 가장 높았으며 또 KOH의 당량에 비례하여 percent conversion도 증가하였다. 그러나 $130^{\circ}C,\;155^{\circ}C$로 중합온도를 상승함에 따라 $CS_2$/KOH mole ratio와 KOH양에는 크게 관계없이 높은 percent conversion을 얻을 수 있었다. 그리고 30分 정도의 짧은 중합시간으로도 $80{\%}$ 이상의 높은 percent conversion을 얻을 수 있었다.

The anionic polymerization of ${\varepsilon}$-caprolactam via $CS_2$/KOH catalysis was carried out under various conditions. The inherent viscosity of the polymers and percent conversion of the polymers were determined. It was observed that the percent conversion was increased as an increasing concentration of catalyst and initiator. The percent conversion was relatively low at low temperature and the highest percent conversion was obtained at temperature between $130^{\circ}C,\;to\;155^{\circ}C$ with any $CS_2$/KOH mole ratio.

키워드

참고문헌

  1. J. Polymer. Sci. v.30 J. Saunder
  2. J. Polymer. Sci. v.30 J. Sebenda
  3. Synthetic heterochain polyamide V.V. Korshak;T.M. Frunze
  4. U.S. Pat. 2,251,519 R.N. Joyce;D.M. Ritter
  5. J. Polymer. Sci. v.3 W. E. Hanford;R. M. Joyce
  6. Angew. Chem. v.54 K. Goldstein
  7. Bull. Chem. Soc. Japan v.31 H. Yumato;N. Ogata
  8. Bull. Chem. Soc. Japan v.31 H. Yumato;N. Ogata
  9. J. Polymer Sci. v.4 T. Konomi;H. Teni
  10. Faserforsch Textiltech v.10 S. Schaaf
  11. J. Polymer Sci. v.7 H. Tani;T. Konomi
  12. Makromol, Chem. v.35 O. Wichterle
  13. J. Polymer Sci. v.43 N. Yoda;A. Miyake
  14. J. Polymer Sci. v.4 Hisaya Tani
  15. J. Polymer Sci. v.4 S. Barzakay;M. Leey;D. Vofsi
  16. J. Korean Chem. Soc. v.20 B. Jung;S.K. Choi;G.S. Suh
  17. J. Korean Chem. Soc. v.20 S.K. Choi;H.K. Suh
  18. J. Korean Chem. Soc. v.21 G.S. Suh;S.K. Choi
  19. C. A. v.54