Abstract
Strain rate dependence of the flow stress of cold-worked and annealed Zircaloy-4 was studied by stress relaxation test in temperature range of 20$0^{\circ}C$ to 45$0^{\circ}C$. The In $\sigma$-ln i curves for various temperatures were straight in the eirange of 10$^{-5}$ to 10$^{-3}$ sec$^{-1}$ . From the slope of a curve strain rate sensitivity m was obtained. The m in cold-worked Zircaloy-4 had a minimum value at 30$0^{\circ}C$, while m in annealed Zircaloy-4 had two minimum values, one at 30$0^{\circ}C$ and the other at 45$0^{\circ}C$. It was found that the temperatures of the minimum m are consistent with the temperatures of strain ageing peaks. The minimum m at 30$0^{\circ}C$ is considered to be due to strain ageing owing to the pinning of glide dislocations by oxygen atoms, while the minimum m at 45$0^{\circ}C$ for annealed specimen is attributed to iron atoms.
질칼로이-4에 있어서 flow stress strain rate 의존성을 냉간가공 및 소둔된 시편에 대해 20$0^{\circ}C$-45$0^{\circ}C$ 온도 구간에서 응력이완 실험으로 조사하였다. 전체 실험온도에서 In-3-ln i 관계식은 $10^{-5}$-$10^{-3}$ sec$^{-1}$ strain rate의 구간에 걸쳐 선형관계를 보였다. 냉간 가공된 질칼로이 -4의 strain rate sensitivity, m값은 30$0^{\circ}C$에서 최소값을 보인 반면, 소둔된 시편의 경우 30$0^{\circ}C$와 45$0^{\circ}C$에서 최소값들을 보였다. 최소값의 m이 나타나는 온도는 가공시효값이 극대값을 보이는 온도와 일치한다는 사실이 확인되었다. m값의 감소는 활동자유전위들이 산소원자에 의해 pinning된 결과로 유발되는 가공 시효와 관련된 것으로 고려된다. 그리고 소둔된 시편이 45$0^{\circ}C$에서 가지는 최소 m값은 철 원자들로 인한 가공 시효에서 기인된 것으로 생각된다.