Effect of active alkali concentration on the delignification of Larch UKP

활성(活性) 알칼리 농도(濃度)가 일본잎갈나무 UKP의 탈(脫)리그닌에 미치는 영향(影響)

This study was carried out in order to obtain the effect of active alkali concentration. Sulfidity 25%, maximum temperature 170$^{\circ}C$, cooking time 3hrs., liquor to wood ratio 5 : 1 in the kraft cooking conditions were maintained. Active alkali concentration were varied at intervals of 3% between 12% and 24%. The rates of de lignification increased with an increase in active alkali concentration and beatability, brightness, and strength of pulp also improved. The total pulp yield trand to decrease with an increase of active alkali concentration. The maximum screened pulp yield were obtained between 18% and 21% A.A.. Therefore, the optimum active alkali concentration was 18~21%.

본실험(本實驗)은 일본잎갈나무재(材)를 공시원료(供試原料)로 하여 UKP 제조시(製造時) 활성(活性)알칼리 농도(濃度)가 탈(脫)리그닌 및 펌프품질에 미치는 영향(影響)을 구명(究明)하여 그 최적(最適) 펄프화 조건(條件)을 확립(確立)코자 실시한 바, 그 결과를 요약(要約)하면 다음과 같다. 1) 일본 잎갈나무재(材)는 비중(比重)이 0.42, 섬유장(纖維長)이 3.34 mm, 섬유폭(纖維幅)이 0.035mm로서 다른 침엽수류(針葉樹類)와 비슷하였다. 2) 일본잎갈나무는 다른 침엽수(針葉樹)와 달리 holocellulose 및 pentosan의 함량(含量)이 낮고 lignin 함량(含量)이 높아 펄프 수율(收率)을 저하(低下)시키는 결점(缺點)을 갖고 있다. 3) 활성(活性)알칼리 농도(濃度)의 증가(增加)에 따라 lignin 함량(含量)과 펄프 수율(收率)이 감소했다. 4) 활성(活性)알칼리 농도(濃度) 18~21%에서 최고(最高)의 정선수율(精選收率)이 나타났다. 5) 탈(脫)리그닌화(化)가 진행(進行)됨에 따라 펄프의 명해성(明解性)이 개선되었다. 6) pulp sheet의 백색도(白色度)는 탈(脫)리그닌정도(程度)와 비례관계가 있었다. 7) 일본잎갈나무 UKP의 비파열도(比破裂度) 및 열단장(裂斷長)은 평균수준 이었으나 비인열도(比引裂度)가 매우 높아 중색열지용(中色裂紙用)으로 적합(適合)하였다. 8) 활성(活性)알칼리 농도(濃度)가 증가(增加)함에 따라 공시(供試)펄프의 제반강도(强度)가 개선되었다.