Effect of Pre-Rolling on the Mechanical Properties of AI-Mg-Mn Alloy

Al-Mg-Mn합금의 기계적(機械的) 성질(性質)에 미친 여비압재(予備圧在)의 영향(影響)

In this work the effect of pre-rolling on the homogenization and on the mechanical properties of 4.6% Mg-0.5% Mn-0.18% Cr-Al alloy has been studied. At room temperature tensile strength and elongation have been found to increase in the pre- rolled homogenized sample compared to those of the as cast sample. At $400^{\circ}C$ this pre-rolled homogenized sample has shown a little lower tensile strength and a remarkably higher elongation than the samples as casted or homogenized without pre-rolling. Metallurgical microstructure of the pre-rolled homogenized sample has shown conspicuously less secondary phase such as ${\beta}$-phase at the grain boundaries than the other samples. The difference of magnesium content between grain boundaries and within the grains has been also checked by EPMA. The test results show enhanced homogenizing effect by the pre-rolling before homogenizing heat treatment.

본 실험에서는 여비압연이 4. 6%Mg-0.5% Mn-0.18%Cr의 알루미늄합금의 균질화처리 및 그의 기계적 성질에 마치는 영향을 조사하였다. 여비압연후 균질화 열처리된 시편은 주조상태의 시편에 비하여 실온 인장강도 및 연신률이 증가되고 있음을 보여주었다. $400^{\circ}C$의 고온 인장시험의 결과는 여비압연후 균질화열처리한 시편이 주조상태 또는 그의 균질화처리만 시행한 것에 비하여 다소 낮은 인장강도와 현저히 향상된 연신률을 소지함을 보여주었다. 여비압연후 균질화열처리된 시편의 금속현미경조직은 다른 시편들에 비해 결정입계에 ${\beta}$ 상등의 제2상이 현저히 감소되고 있음을 나타내고 있다. 시편의 결정입내 및 입계에 있어서의 주된 합금첨가원소인 Mg 분포상태를 EPMA를 사용하여 조사하였다. 이 결과는 균질화처리를 시행하기 전에 여비압연을 도입함으로써 균질화처리의 효과가 증대되고 있음을 보여주고 있다.