Study on the Preferred Orientation Using White Neutron

The previous expression for the diffracted neutron intensity by a highly oriented polycrystalline is modified using the Kunitomi's formula of the crystal reflectivity The method of studying the preferred orientation in metals with white neutron is proposed utilizing the above formula and the fact that the real position of the diffraction of certain grain in the sample can be found by the comparison of the smaller angle part of the maxwellian curve of the calculated intensity of neutrons diffracted and the experimenal curves. The most probable wavelength of thermal neutrons from the reactor is found by the measurement of the neutron spectrum with the correction for the crystal about the multiple reflection and the absorption of neutrons and turned out to be 1.025 $\pm$ 0.001$\AA$. The preferred orientations of some electric steel sheets, mostly with the cube-on-face orientations, are investigated by the present method. The orientations of most grains relative to the rolling directions are found to be within 5 degrees. It is found the most of theories for large crystals may be extended to highly oriented polycrystalline materials without extensive modification.

강한 방향성이 있는 다결정에 의한 중성자회절강도에 대한 재래의 공식을 결정의 반사율에 관한 Kunitomi 의식을 사용하여 수정하였다. 시료내의 grain 에서 회절이 일어나는 정화한 위치가 회절강도의 Maxwell곡선의 소각부분에 관한 이론치와 계산치를 비교함으로써 발견된다는 사실과 위의 회절강도 공식을 사용하여 금속내의 Preferred orientation을 백색중성자를 가지고 조사한 수 있는 방법을 고안하였다. 결정 내에서 일어나는 중성자비 다중반사와 흡수에 대해서 교정하여 원자로의 중성자 스펙트럼을 측정함으로써 열중성자의 확실성있는 파장이 1.025$\pm$0.001$\AA$임을 알았다. 대부분 cube-on-face 방향을 갖인 씰리콘 강철을 본 연구방법으로 조사차였는바 grain들이 압연방향에서 5도 이내에 배열되어 있다는 사실을 발견하였다. 커다란 결정에 적합한 이론들이 강한 방향성이 있는 다결정 물체에도 적응될 수 있음을 알게 되었다.