Abstract
"Rapid Determination of Boric Acid in Nickel Plating Solution" by the addition of Na$_2$C$_2$O$_4$ and thus preventing the precipitation of i(OH)$_2$ during titiration , has previously been reported. In this paper, the exact amount of glycerine and the complexing possibility of oxalate with nickel has been determined by measn of conductivity titrations. This experimental work has been supported by the mathematical application of the Debye-Huckel and mass action equitions as well as statistical analysis. The results were ; (1) Fro determining boric acid in nickel plating solution, 20 ml of 400ml/ι glycerine was sufficient, since 97% of the H$_3$BO$_3$ was dissoicated by this addition. (2) In the absence of Na$_2$C$_2$O$_4$ the continious precipitation of Ni(OH)$_2$ during titration with NaOH even past end -point for boric acid determination resulted in considerable anlaytical error. (3) In the presence of Na$_2$C$_2$O$_4$ during titration , Ni++ combined with C$_2$O$_4$-to form NiC$_2$O$_4$. The solution with this precititate of very fine, colloidal , trantsparent particles, remained quite clear for approximately 2 hours. Therefore it was shown that the presence of Na$_2$C$_2$O$_4$ prevents the formation of gross Ni(OH)$_2$ precititation by forming NiC$_2$O$_4$ instead of a complex salt with Ni++ , which did not interfere with the visible determination of the end point for boric acid with NaOH titation. This observous may be interpreted in the light of the previously published solubility ratio for NiC$_2$O$_4$ and Ni(OH)$_2$, 0.3mg/100g H$_2$O(25$^{\circ}C$), respectively. Precipitation of the less soluble , albeit transparent salt, NiC$_2$O$_4$ precluded therefore the precipitation of the Ni(OH)$_2$ salt.