Abstract
Deformation modes at room temperature and the interaction between slip lines and ${\gamma}$' precipitate particles in heat treated Rene 41 were studied by means of replica techniques in an electron microscope. The alloy had been deformed by compression after aging for times up to 9300 hr at 76$0^{\circ}C$ and 87$0^{\circ}C$. The slip structure observed was similar to that of o brass, i.e., consisting of single slip lines occurred on the｛111｝<110> system. The slip structure was also correlated with aging conditions. Slip lines appeared to pass through ${\gamma}$' particles, shearing them with the matrix even after a prolonged heat treatment. It was concluded on the basis of comparison with previously published data that ${\gamma}$' particles remain at least partially coherent with the matrix even in a greatly overaged condition.
닉켈기 내열합금의 일종인 Rene 41을 76$0^{\circ}C$ 및 87$0^{\circ}C$에서 최고 9300 시간까지 시효열처리한 다음, 5% 내지 20%로 압축변형시켜, 이 합금의 실온에서의 소성변형방식 및 석출입자인 ${\gamma}$'입자와 slip line 간의 상호작용을 전자현미경적 방법으로 관찰연구하였다. 본합금의 slip구조는 $\alpha$황동때와 유사하게｛111｝<110>계에 속하는 단일 slip line으로 구성되어 있었으며, 순알루미늄에서 관찰되는 층상구조는 볼 수 없었다. 또한, slip 구조는 시효조건에 따라 변화한다는 것을 알 수 있었다. 미시효상태뿐만 아니라 과시효상태에 있어서도 Slip line은 여전히${\gamma}$' 석출입자를 통과하였으며, 이 때 석출입자는 지금과 더불어 변형되는 것을 볼 수 있었다. 이 관찰결과를 앞서 발표된 자료와 비교 검토하여 과시효상태에서도 ${\gamma}$'입자는 적어도 일부 지금과 정합되어 있다는 결론을 얻었다.