초록
The back contact solar cell (BCSC) has several advantages compared to the conventional solar cell since it can reduce grid shadowing loss and contact resistance between the electrode and the silicon substrate. This paper presents the effect of the surface texturing of the silicon BCSC by varying the texturing depth or the texturing gap in the commercially available simulation software, ATHENA and ATLAS of the company SILVACO. The texturing depth was varied from $5{\mu}m$ to $150{\mu}m$ and the texturing gap was varied from $1{\mu}m$ to $100{\mu}m$ in the simulation. The resulting efficiency of the silicon BCSC was evaluated depending on the texturing condition. The quantum efficiency and the I-V curve of the designed silicon BCSC was also obtained for the analysis since they are closely related with the solar cell efficiency. Other parameters of the simulated silicon BCSC are as follows. The substrate was an n-type silicon, which was doped with phosphorous at $6{\times}10^{15}cm^{-3}$, and its thickness was $180{\mu}m$, a typical thickness of commercial solar cell substrate thickness. The back surface field (BSF) was $1{\times}10^{20}\;cm^{-3}$ and the doping concentration of a boron doped emitter was $8.5{\times}10^{19}\;cm^{-3}$. The pitch of the silicon BCSC was $1250{\mu}m$ and the anti-reflection coating (ARC) SiN thickness was $0.079{\mu}m$. It was assumed that the texturing was anisotropic etching of crystalline silicon, resulting in texturing angle of 54.7 degrees. The best efficiency was 25.6264% when texturing depth was $50{\mu}m$ with zero texturing gap in case of low texturing depth (< $100{\mu}m$).