냉간 박판압연공정에서 공정변수가 엣지 크랙 성장에 미치는 영향

Effect of process parameters on propagation of edge crack in the cold rolling

Edge cracks in cold rolling always influence to the quality of productions, while the "V" shaped cracks were propagated by passing the roll gap. We set up the sizes and shapes of initial cracks in simulation according to the references from real productions. Different to in hot rolling, the cracks in cold rolling couldn't be reduced from propagation automatically after generated, even if these could be reduced by changing the process parameters. In this paper, we described the affections of process parameters on the propagation of edge cracks, such as reduction ratio and tension. We predicted that the dependence of the cracks propagations of changing of process conditions and expected to gain the smaller edge cracks. By raising the reduction ratio, the cracks were propagated increasingly in both transverse and rolling directions. And as tension raise, the cracks became propagated in both directions in which transverse direction was less effectively.