Electrical and optical properties of AZO films sputtered in $Ar:H_2$ gas RF magnetron sputtering system

AZO films were prepared by $Ar:H_2$ gas RF magnetron sputtering system with a AZO (2wt% $Al_2O_3$) ceramic target at a low temperature of $100^{\circ}C$. To investigate the influence of $H_2$ flow ratio on the properties of AZO films, $H_2$ flow ratio was changed from 0.5% to 2%. As a result, the AZO films deposited with 1% $H_2$ addition showed electrical properties with a resistivity of $5.06{\times}10^{-3}{\Omega}cm$. The spectrophotometer-measurements showed the transmittance of 86.5% was obtained by the film deposited with $H_2$ flow ratio of 1% in the range of 940nm for GaAs/GaAlAs LED.