Performance variation of catalyst for hydrogen peroxide thruster with drying condition

과산화수소 추력기용 촉매의 건조 조건 변화에 따른 성능 변화

In this paper, performance evaluation of catalyst for hydrogen peroxide thruster with drying condition is described. Platinum was selected as a catalyst, and alumina of pellet type was chosen as a catalyst support. Evaporation method known as general method for catalyst production was used to make the catalyst. From previous experiments, it is favorable during catalyst making process that solution of active material has low pH level. Therefore, some kinds of low pH level solution had been tested. The drying temperatures are 25, 50, 70, and $90^{\circ}C$. From experimental results, it shows better performance that drying temperature was $90^{\circ}C$ since the catalyst particle could not be crystallized but be evenly spreaded out due to the rapid evaporation of solvent.

과산화수소를 일원 추진제로 사용하는 추력기용 촉매의 건조 조건에 따른 성능 변화에 대한 실험을 수행하였다. 사용한 촉매는 백금이며 촉매 지지체는 펠렛 타입의 알루미나이다. 일반적인 촉매 제작 방법인 증발건조법을 사용하였으며, 이 때 건조 조건에 따른 촉매의 성능을 평가하였다. 촉매 제작 조건 중 pH 값이 낮은 경우 촉매 제작이 유리하였기 때문에 다양한 산성 용액에서 촉매를 담지 해 실험을 수행하였다. 건조 온도는 각각 25, 50, 70, $90^{\circ}C$이며 실험 결과 $90^{\circ}C$에서 건조한 경우 높은 성능을 보임을 알 수 있었다. 이는 빠른 증발속도로 인해서 백금이 결정화를 이루지 못하고 고르게 분산되었기 때문으로 판단된다.