Studies on Incombustibility Improvement of EPDM Rubber with $Al(OH)_3$ and $Sb_2O_3$

$Al(OH)_3$와 $Sb_2O_3$의 첨가에 따른 EPDM계 고무의 난연성 향상 연구

In order to improve incombustibility of EPDM(Ethylene propylene diene monomer)-based rubber, inorganic materials as $Al(OH)_3$ and $Sb_2O_3$ were added. The mechanical and thermal properties have been measured for vulcanized rubber loaded with different concentrations of $Al(OH)_3$ and $Sb_2O_3$. As inorganic material contents increases from 5phr to 30phr, the specific gravity and hardness increase while elongation at break decreases. This study performed incombustibility test and thermal analysis through TGA(Thermogravimetric Analyzer). As a results, incombustible and thermal properties of EPDM-based rubber were improved as $Al(OH)_3$ and $Sb_2O_3$ contents increase.

EPDM(Ethylene-propylene diene monomer)계 고무의 난연성 향상을 위하여 무기계 난연재료인 $Al(OH)_3$와 $Sb_2O_3$를 첨가하여 물성 및 열적 특성을 조사하였다. 각 시편의 물성은 큰 차이를 보이지 않았으나, 난연재료의 함량이 증가할 수 록 비중과 경도는 높아지는 반면에 신율은 낮아지는 경향이 있었다. 본 연구에서는 열분석과 난연성 시험을 실시하였고, 결과적으로 난연재료의 함량이 10phr 이상에서는 난연 효과가 확연히 나타나는 것으로 판단되었다.