RF 스퍼터링에 의한 ITiO 박막 제작과 태양전지에의 응용

Synthesis of titanium-doped indium oxide (ITiO) films for solar cells application using RF magnetron sputtering technology

Transparent conductive metal oxide films of $In_{2-x}Sn_xO_3$ (ITiO) and $In_{2-x}Sn_xO_3$ (ITO) were deposited by RF magnetron sputtering at relatively low substrate temperature (~$300^{\circ}C$) and at high rate (~10nm/min). Electrical and optical properties of the films were investigated as well as film structure and morphology, as it is compared with the commercial F:$SnO_2$ (FTO) glass. Near infrared ray transmittance of ITiO is the highest for wavelengths over 1000nm, which can increase dye sensitized compared to ITiO and FTO. Dye-sensitized solar cells (DSCs) were fabricated using the ITiO, ITO and FTO. Photoconversion efficiency ($\eta$) of DSC using ITiO is 5.5%, whereas 5.0% is obtained from DSC with ITO, both at 100mW/$cm^2$ light intensity.