The Experimental Study on The Compressive Strength of Mortar Using High Quality Recycled Fine Aggregate Produced by Sulphuric Water and Low Speed Wet Abraser

황산수와 저속습식마쇄기로 생산된 고품질 순환 잔골재의 모르타르 압축강도에 관한 실험적 연구

  • Published : 2008.04.24

Abstract

Recycled fine aggregate has low quality because it contains large amount of old mortar. So, its usage is limited to a lower value-add, such as the roadbed material etc. Also, alkaline water occurred from treatment process of the waste concrete is becoming the cause of environmental problem. Accordingly, this study is to develop on the high quality recycled fine aggregate produced by low speed wet abraser using sulphuric. We investigated the properties of compressive strength of the mortar which was manufactured using recycled fine aggregate containing calcined gypsum produced by earlier mentioned process. Test results indicate that mortar using recycled fine aggregate containing calcined gypsum has lowest compressive strength. It seems that low compressive strength is closely associated with the expansion of the specimen by excessive formation of ettringite.

현 국내에서 생산되고 있는 대다수의 순환잔골재는 골재표면에 부착되어 있는 폐모르터 성분으로 인하여 낮은 밀도와 높은 흡수율의 물리적 특성을 나타내는 저품질 골재이다. 이러한 이유로 일반 콘크리트용 골재 또는 콘크리트 제품제조용 골재로 사용이 부적합하며 일반 성토, 매립재용으로 사용되고 있는 실정이다. 또한 골재 세척에 사용되는 공정수는 골제 세척 후 강알칼리성을 띠게 되어 추가적인 처리비용이 발생한다. 이러한 문제점을 해결하기 위하여 기존 파 분쇄 방법이 아닌 마쇄 방법을 사용하여 골재간의 마찰과 자유낙하에 의한 운동동에너지로 골재표면에 폐모르터 성분을 탈리시키고 황산수를 공정수로 사용함으로써 중화반응에 의해 중성 또는 약산성화 하는 방법으로 고품질 순환잔골재를 생산하였다. 상기의 방법으로 생산된 순환 잔골재는 폐모르터 성분에 포함되어있는 $Ca(OH)_2$와 공정수에 투입한 $H_2SO_4$의 중화반응에 의해 반응생성물인 석고가 생성되고, 중화반응에 의해 생성된 석고는 재생골재를 건조하는 과정에서 반수석고로 변환된다. 일반적으로 시멘트에 포함된 석고는 응결을 완화 할 뿐 아니라 단기강도를 높이고 건조수축을 감소시키며, 화학적 저항성을 향상시키는 등의 효과가 알려져 있다. 이에 본 연구는 황산수와 습식마쇄를 이용하여 생산된 순환골재에 포함되어 있는 반수석고가 모르터의 압축강도에 미치는 영향을 검토하였다. 실험 결과, 반수석고가 포함된 고품질 순환잔골재의 경우 석고를 제거한 고품질 순환 잔골재에 비해 과도한 에트링자이트 생성으로 인하여 수화생성물의 치밀한 구조를 와해시켜 압축강도 및 휨 강도가 저하되는 것으로 나타났다.

Keywords