Mixing and Strength Properties of 150MPa Ultra High Strength Concrete

150MPa 초고강도 콘크리트 배합 및 강도발현 특성

Ultra High Strength Concrete(UHSC) is necessary a clear presentation about mechanical property that is different from normal strength concrete and an evaluation of serviceability of high rise building which is used ultra high strength concrete. To mixing ultra high strength concrete with $f_{ck}$=150MPa pre-mix cement were manufactured and experimental study were conducted to evaluated on the mixing properties and compressive strength with major variables as unit cement contents, water-binder ratio and type of pre-mix cement. As a test result, it is shown that the concrete mixing time is required about 5$^{\sim}$6 minute untill the each materials(ordinary portland cement, silica fume, blast-furnace slag powder and anhydrite) are revitalized enough. A slump flow of fresh concrete are shown about 700$^{\sim}$750mm with proper viscosity. And average value of concrete compressive strength are shown about 77% in 7days, 87% in 14days and 102% in 56days for 28days of concrete material age. From this experimental study, a proper mixture proportion of pre-mix cement are recommended about 54$^{\sim}$59% OPC, 25$^{\sim}$30% blast-furnace slag powder and 10$^{\sim}$15% silica fume for mix the ultra high strength concrete with $f_{ck}$=150MPa.

150MPa 수준의 초고강도 콘크리트를 제조하기 위하여 프리믹스형태의 시멘트를 제조하였고, 각 시멘트의 특성별로 초고강도 콘크리트 배합특성과 재령별 강도발현 특성을 비교하였다. 실험결과 콘크리트의 배합에 소요되는 시간은 콘크리트 각 재료가 충분히 활성화되기까지 대략 5분에서 6분 사이에 콘크리트 믹싱이 완료되는 것으로 나타났다. 콘크리트의 압축강도는 재령 28일을 기준으로 7일에서는 77%, 14일에서는 87%정, 56일에서는 약 102%정도로 나타났으며, 150MPa 정도의 초고강도 콘크리트 제조를 위하여 OPC는 54%내외, 슬래그미분말은 25${\sim}$30%, 실리카흄은 10${\sim}$15% 정도의 범위에서 프리믹스시멘트를 제조하여 콘크리트 배합에 적용할 수 있을 것으로 판단된다. 그리고 초고강도 콘크리트는 매우 큰 점성을 가질 수 있어 이러한 점성과 콘크리트 타설 및 작업과의 상관성을 고려하여 플로우치는 700${\sim}$750mm정도를 확보하여야 할 것으로 판단된다.