A Study on Properties of Ultra High Strength Concrete of above 100MPa

100MPa급 이상의 초고강도 콘크리트의 자기수축 특성에 관한 연구

The autogenous shrinkage of HPC is important in that it can lead the early cracks in concrete structures. The purpose of the present study is to explore the autogenous shrinkage of HPC with cellulose fiber and expansive additive and to derive a realistic equation to estimate the autogenous shrinkage model of that. For this purpose, comprehensive experimental program has been set up to observe the autogenous shrinkage for various test series. Major test variables were the quantity of expansive additive and cellulose fiber. Water-cement ratio is fixed with 13%. The autogenous shrinkage of HPC is found to decrease with increasing expansive additive and cellulose fiber. A prediction equation to estimate the autogenous shrinkage of HPC was derived and proposed in this study. The proposed equation shows reasonably good correlation with test data on autogenous shrinkage of HPC.

최근 초고강도와 고유동성을 가진 고성능 콘크리트에 대한 연구가 활발히 진행되고 있으며, 사용 실적도 점차 증가하는 추세에 있다. 그러나 고성능 콘크리트의 경우에는 수화열 이외에 자기수축으로 인해 균열이 발생하는 경우가 있어 고성능 콘크리트의 균열제어 및 설계에서 자기수축 변형을 반드시 고려해야 한다. 이에 따라, 본 연구에서는 셀룰로스 칩 화이바 및 팽창재를 혼입한 고성능 콘크리트의 자기수축 특성에 대한 실험 연구를 통해 자기수축 예측모델을 제안하고자 한다. 주요 실험변수는 팽창재 및 셀룰로스 칩 혼입률로 설정하였으며 물-시멘트 비는 13%로 고정하였다. 콘크리트의 유동성, 압축강도 및 자기수축 실험을 수행하였으며 팽창재 및 셀룰로스 칩 화이바의 혼입량이 클수록 고성능콘크리트의 자기수축 길이변화율이 감소하는 경향을 보였다.