Evaluation of the Flowability and Compressive Strength of Alkali-Activated Blast Slag Mortar

고로슬래그 알칼리 활성 모르타르의 유동성 및 압축강도 평가

Many researches on alkali-activated concrete that does not need the presence of cement as a binder have been carried out recently. Instead, the source of material such as fly ash and blast slag, that are rich in Silicon(Si) and Aluminium(Al), are activated by alkaline liquids to produce the binder. Hence concrete with no cement is effect reduction of CO$_2$ gas. In this study, we investigated the influence of the workability and compressive strength of mortar on water reducing agent, alkaline activator and curing method in oder to develop cementless blast slag based alkali-activated mortar. In view of the results, we found out that the flowability of mortar was lowered as increasing to mole concentration of NaOH, but not large the loss of flowability to 9M NaOH, most of water reducing agent was not effect. The compressive strength was improved as increasing to mole concentration of NaOH, was the most effect in 9M NaOH. The curing temperature and curing conditions on compressive strength of blast slag based alkali-activated mortar didn't influence.

최근 결합재로 시멘트를 사용하지 않은 알칼리 활성 콘크리트에 대한 연구가 활발히 진행되고 있다. 이 알칼리 활성 콘크리트는 시멘트 대신에 실리콘(Si)과 알루미늄(Al)이 풍부한 플라이애시와 고로슬래그등을 사용하여 알칼리 용액으로 활성화시킨 시멘트 ZERO 콘크리트로서 CO$_2$ 가스를 저감하는데 효과적이다. 본 연구에서는 시멘트를 전혀 사용하지 않고 결합재로서 고로슬래그를 100% 사용한 알칼리 활성 콘크리트를 개발할 목적으로 감수제, 알칼리 활성화제 및 양생조건이 모르타르의 시공성 및 압축강도에 미치는 영향에 대해 검토하였다. 그 결과, NaOH의 몰 농도가 증가함에 따라 유동성은 저하되나, 9M까지는 유동성 저하가 크지 않고, 대부분의 감수제는 유동성 향상에 기여하지 못하는 것으로 나타났다. 그리고 압축강도는 NaOH의 몰 농도가 증가함에 따라 향상되나, 9M이 가장 효율적인 것으로 나타났다. 또한 양생온도 및 양생조건은 고로슬래그 알칼리 활성 모르타르의 강도에는 큰 영향이 없는 것으로 나타났다.