Hydration heat and autogenous shrinkage properties of silica-fume included mass concrete

실리카퓸을 사용한 매스콘크리트의 수화열과 자기수축 특성

Adiabatic temperature rise and autogenous shrinkage experiments were performed for three silica-fume included mass concrete mixtures and a reference mixture without silica-fume, in order to investigate the influence of silica-fume on the hydration heat and autogenous shrinkage properties of mass concrete, and to examine applicability of silica-fume to mass concrete. It was revealed from the experiment that, for mass concrete, the rate of hydration was hardly increased while the maximum adiabatic temperature rise decreased about 5$^{\circ}$C by the addition of silica-fume, and the amount of autogenous shrinkage was almost the same regardless of silica-fume replacement. These facts imply that silica-fume can enhance the resistance of mass concrete to temperature cracking as well as the durability.

물/결합재비가 0.4이면서 5%의 실리카퓸이 혼입된 3가지 매스콘크리트 배합과 실리카퓸이 혼입되지 않은 1가지 매스콘크리트 배합에 대해 단열온도상승실험과 자기수축실험을 실시하여 실리카퓸이 매스콘크리트의 수화발열특성과 자기수축에 미치는 영향을 규명하고, 그 결과를 통해 실리카퓸의 매스콘크리트에 대한 적용 가능성을 검토하였다. 실험결과, 매스콘크리트 배합의 경우에는 실리카퓸을 혼입하여도 수화반응속도가 거의 증가하지 않으면서 최종단열온도상승량이 5$^{\circ}$C 정도 감소하는 것으로 나타났으며, 콘크리트의 극한자기수축량은 실리카퓸의 혼입여부에 상관없이 거의 동일한 것으로 나타났다. 따라서 실무에서 매스콘크리트 구조물의 시공에 실리카퓸을 적용하면 내구성뿐만 아니라 수화열 균열제어에도 이점이 있을 것으로 판단된다.