Mock-up Test for Field Application of a Polylon Fiber Method

폴리론 화이버 공법의 현장적용을 위한 Mock-up Test

This study, as mock-up test for applying Polylon Fiber engineering method to the field, analyzed the fundamental characteristics and the fireproof characteristics of high strength concrete mixed with Polylon Fiber 0.05% and the results are summarized as followings. From the characteristic of the fresh concrete, both slump flow and air content were appeared to satisfy target range. And from the characteristic of hardened concrete, all compressive strengths according to the curing conditions were appeared to satisfy design standard strength of 60 MPa. From the fireproof characteristic, small scaling and spalling phenomenon were partially appeared on the surface part of specimens, but generally the excellent fireproof capacities were appeared. From the characteristic of temperature hysteresis, the highest temperature and the average temperature of reinforcing part after fire-resistant test for 3 hours were $531^{\circ}C$ and $405{\circ}C$, respectively and then satisfied fireproof standard of the Ministry of Land Transportation and Maritime Affairs.

본 연구는 폴리론 화이버 공법의 현장 적용을 위한 Mock-up 실험으로, 폴리론 화이버 0.05% 혼입한 고강도 콘크리트의 기초적 특성 및 내화특성에 대해 분석하였는데, 그 결과를 요약하면 다음과 같다. 굳지않은 콘크리트의 특성으로, 슬럼프플로우 및 공기량은 모두 목표 범위를 만족하는 것으로 나타났고, 경화 콘크리트의 특성으로 양생 조건에 따른 압축강도는 모두 설계기준강도 60 MPa 만족하는 것으로 나타났다. 내화특성으로, 시험체의 표면부에 일부 약간의 박리 폭렬 현상이 나타났지만, 전체적으로는 양호한 내화성능을 나타내었다. 온도이력 특성으로, 3시간 내화시험 후 주근부 최고온도 $531{\circ}C$, 평균온도 $405{\circ}C$로 국토해양부의 내화기준을 만족하였다.