Characteristics of Chloride Penetration in Cracked Flexural Member using Durable Materials

고내구성 재료를 사용한 휨부재의 균열에 따른 염화물 침투 특성

Crack is a penetration path of harmful material such as chloride ion, and causes a serious deterioration in durability. So, the characteristics of chloride penetration are investigated for the cracked flexural concrete members using high-durable materials. For these, the flexural crack of beam specimen is introduced by transverse loading. And, Rapid Chloride Penetration Test (RCPT) and Long-term chloride penetration test are carried out to compare the chloride penetration depth. From test results when crack is happened, the chloride penetration resistance of the durable member was superior than that of the normal member. Blast furnace slag concrete member has a excellent chloride penetration resistance in long-term chloride penetration test.

균열은 콘크리트에 염소이온과 같은 유해한 물질의 침투경로가 되어 내구성에 심각한 열화를 야기한다. 따라서 고내구성 재료를 사용한 콘크리트 휨부재에서의 균열 발생에 따른 염소이온 침투특성을 검토하고자 하였다. 이를 위해, 고내구성 재료를 적용한 보에 하중을 가하여 휨균열을 도입시키고, 촉진 염화물 침투실험(RCPT)과 장기 염화물 침투실험을 실시하여 염화물 침투 특성을 파악하였다. 실험결과에 따르면, 고내구성 재료를 적용한 부재는 균열이 발생하여도 일반 콘크리트 부재에 비해 높은 염화물 침투 저항성을 보였다. 특히 고로슬래그 미분말을 적용한 경우, 균열 부재의 장기 염화물 침투 실험에서 탁월한 염화물 침투 저항성을 보였다.