Abstract
MgO powder-mixed concrete, expanded at the lower temperature around $850{\sim}1000$ degree celcius, might have long-term expansibility, which could remunerate for the contraction of concrete with delayed expansion, and through the process, the crack resistance of mass concrete might be improved. Currently used expandable concrete additive has three different types : CSA, CaO and MgO. In this study, therefore, such tests as carbonation, chloride diffusivity, freezing-thawing resistance and sulfate resistance after 56 days' curing were implemented and compared the results with the concrete with no MgO mixed to evaluate the durability of 5% MgO-mixed concrete after longer period of time. The degree of hydration for the MgO-mixed cement paste was analyzed after 1 day, 3 days, 7 days, 28 days, and 56 days using SEM, XRD, DSC.
$850^{\circ}C{\sim}1000^{\circ}C$ 정도의 저온에서 소성된 MgO 분말을 사용한 콘크리트는 장기적인 팽창성을 가지게 되며, 이러한 팽창의 특성은 지연팽창을 통하여 콘크리트의 수축을 보상하는 특성을 지니게 된다. 이를 통하여 매스 콘크리트의 균열저항성능의 개선 효과를 기대할 수 있다. 현재 사용되는 팽창성 콘크리트 혼화재료는 에트린자이트형(CSA), 산화칼슘(CaO)형, 산화마그네슘형(MgO)가 있다. 본 연구에서는 5%의 MgO를 사용한 콘크리트의 장기재령에서의 내구특성을 평가하기 위하여 56일 양생한 후 탄산화, 염화물 확산계수, 동결융해 저항성, 황산염 저항성 실험을 실시하여, MgO를 혼합 하지 않은 콘크리트와 비교하였다. 또한 10%의 MgO를 넣은 시멘트 페이스트를 대상으로 1일, 3일, 7일, 28일, 56일에 수화정도를 SEM, XRD, DSC 등을 통하여 분석하였다.