An Experimental Study on Quality Properties of High Strength Concrete by the Replacement ratio Meta-kaolin Usable as Substitutes of Silica-fume

실리카흄 대체재로 활용 가능한 메타카올린의 치환율에 따른 고강도 콘크리트의 품질특성에 관한 실험적 연구

As the high-rise building increase due to the gravitation of population to big cities recently, it requires high quality and high performance of Concrete. As a result, people are keenly interested in Meta-kaolin as new admixture favorable from an economic perspective, which has strength and endurance with admixture at the same level like Silicafume. Accordingly, as to Meta-kaolin, this study was to set by three levels like domestic one, foreign one, and Silicafume, the waterbinding material ratio 25%, and four level substitute like 0, 10, 20, and 30(%) in order to compare and analyze the quality characteristics of high-strength concrete according to the substitute of Meta-kaolin applicable with replacement of Silicafume. As a result of performing experiment, as to the higher the additive amount of Superplasticizing agents in order to secure target liquidity was, the more the substitute in each admixture increased. This study had a tendency that the Silicafume increased the additive amount of Superplasticizing agents with high fineness compared with Meta-kaolin. In addition, the higher the substitute in each admixture was, the more its strength increased On the strength property, the higher the substitute in each admixture was, the more its strength increased. This study has found out that the Meta-kaolin has shown the better strength than the one of Silicafume. On the other hand, the relationship between the Compressive strength and Elastic coefficient has shown the similar formula suggested from ACI363.

최근, 도시 집중화로 인한 초고층 건축물이 증대됨에 따라 콘크리트의 고품질 및 고성능화가 요구 되어 혼화재로 실리카흄과 같은 수준의 강도와 내구성을 확보하며, 경제적인 측면에서 유리한 메타카올린이 새로운 혼화재로 관심이 높아지고 있다. 따라서, 본 연구에서는 실리카흄 대체재로 활용 가능한 메타카올린의 치환율에 따른 고강도 콘크리트의 품질특성을 비교 분석하기 위하여 메타카올린은 국내산, 국외산 및 실리카흄의 3수준과 물-결합재비는 25%, 치환율은 0, 10, 20, 30(%)의 4수준으로 설정하였다. 실험을 실시한 결과, 목표 유동성 확보하기 위한 고성능감수제의 첨가량은 각 혼화재의 치환율이 높아질수록 증가하였으며, 메타카올린이 실리카흄의 높은 분말도로 인해 고성능감수제의 첨가량은 감소하는 경향을 나타내었다. 강도특성에서는 각 혼화재의 치환율이 높아질수록 강도가 증가하였으며, 메타카올린이 실리카흄에 비해 우수한 강도를 나타내었다. 한편, 압축강도와 탄성계수의 관계는 ACI363에서 제시한 식과 유사하게 나타났다.