비냉각 검출기를 위한 BSCT 후막의 제작과 특성 분석

The fabrication and analysis of BSCT thick films for uncooled infrared detectors

$(Ba_{0.57}Sr_{0.33}Ca_{0.10})TiO_3$ (BSCT) thick films doped with 0.1 mol% $MnCO_3$ and $Yb_2O_3$ ($0.1{\sim}0.7$ mol%) were fabricated by the screen printing method on the alumina substrate. And the structural and electrical properties as a function of $Yb_2O_3$ amount were investigated. The lattice constants of the BSCT thick film doped with 0.1 mol% is 0.3955 nm. The specimen doped with 0.7 mol% $Yb_2O_3$ showed dense and uniform grains with diameters of about 6.3 mm. The thickness of all BSCT thick films was approximately 60 mm. The Curie temperature of the BSCT specimen doped with 0.1 mol% $Yb_2O_3$ was $18^{\circ}C$, and the dielectric constantand dielectric loss at this temperature was 4637 and 4.2%, respectively. The BSCT specimen doped with 0.1 mol% $Yb_2O_3$ showed the maximum value of $349{\times}10^{-9}C/cm^2K$ at Curie temperature. The figure of merit $F_D$ for specific detectivity of the specimens doped with 0.1 mol% $Yb_2O_3$ showed the highest value of $10.9{\times}10^{-9}Ccm/J$.