Manufacturing Process Effect on Fatigue Properties for Copper Thin Film

구리박막의 피로특성에 관한 제조공정의 영향

The copper film coated by Sn is often used in various applications such as LCD, Mobile Phone and etc. Especially, when the film is used as tape carrier package(TCP) of LCD panel, the film is repeatedly applied by mechanical or(and) thermal stress and then is often failed. Therefore, to guarantee the reliability of the electrical devices using the film, the tensile and fatigue characteristics of the film are important. In this study, to obtain the tensile and fatigue characteristics of the film, the specimen was fabricated by etching process to make a smooth specimen of 2000 ${\mu}m$ width, 8000 ${\mu}m$ length and 15.26 ${\mu}m$ thickness. The 2 kinds of specimen were fabricated by other manufacturing process. These specimens had values of Young's modulus(80.2GPa) lower than literature values(108${\sim}$145GPa) for bulk values, but had high values of the yield and ultimate strength as 317MPa and 437MPa, respectively. And fatigue test of load-control with 20Hz frequency was performed.