Improved performance of PEDOT:PSS/pentacene Schottky diode on EAPap

셀룰로우스 기반의 EAPap 작동기의 PEDOT_PSS/Pentacene를 이용한 Schottky diode 성능 개선

Pentacene was dissolved in N-methyspyrrolidone (NMP) and mixed with poly(3,4-ethylenedioxythiophene), poly(styrenesulfonate) (PEDOT:PSS). The solution color changed from deep purple to intense yellow. As the dissolution time increased, visible absorption decreased and ultraviolet (UV) absorption increased. PEDOT:PSS or Pentacene-PEDOT:PSS was spin-coated to control the layer thickness. Three-layered Schottky diodes consisting of Al, PEDOT:PSS or PEDOT:PSS-pentacene, and Au with thickness of 300nm, respectively, were fabricated. The current densities of $4.8{\mu}A/cm^2$ at 2.5MV/m and $660{\mu}A/cm^2$ at 1.9MV/m were obtained for the Au/PEDOT:PSS/Al and Au/Pentacene-PEDOT:PSS/Al Schottky diodes, respectively. The current density of the Schottky diode was enhanced by about two orders of magnitude by doping pentacene to PEDOT:PSS.