A Fundamental Study on the Application of High Quality of $TiO_2$ as Architectural materials - Properties of Water purification with as the central -

건축용 재료로서 이산화티탄의 활용성 검토에 관한 기초적 연구 - 수질정화특성을 중심으로 -

Photocatalyst reaction has limit of its usage because application range mostly centered on atmosphere purification area. Thus, it is true that an alternative plans are necessary to increase usage of $TiO_2$ as photocatalyst material. (1) The result of flow felt according to $TiO_2$ replacement rate has shown that both of anatase type and rutile type over 12% deviated from desired flow, $110{\pm}5mm$. Consequently, the range below 9% will be suitable when the anatase type $TiO_2$ if used for functional additives if workability is considered. (2) After compressive strength test, replacement rate 6-9% is estimated as suitable range if $TiO_2$ is used as compressive strength material. Rutile type and anatase type are suitable for in early-age strength and long-age strength respectively. (3) It was revealed that bending strength was dramatically decreased when replacement rate was increased. The main reason were the increase of $TiO_2$ doesn't influence hydration reaction and the decrease of bending strength. (4) The result from the water purification properties test using ion-chromatograhpy has shown that the condition with anatase type $TiO_2$ was normally better than rutile type on the same replacement rate.