Properties of Sandwich Panel Using Cellular Concrete

기포콘크리트를 사용한 샌드위치 패널의 특성

This study sought to investigate the characteristics of cellular concrete, such as porosity, strength and density, according to the cell addition rate. Based on the result, it examined the application to a cellular concrete panel. Porosity was found to increase according to the cell addition rate, measuring continuous porosity of 42% and 47%, and total porosity of 61% and 66%. In terms of cell addition rate, measurements were 7% and 11% respectively. Compressive strength represented 5.0MPa, 3.8MPa and 2.8 MPa in terms of 7%, 9% and 11% respectively, decreasing 1 MPa of strength according to every 2% increase of cell addition rate. Density showed 0.55, 0.44 and 0.36 in terms of 7%, 9% and 11% respectively, decreasing 1.0 MPa according to every 2% increase of cell addition rate proportionally. In addition the sandwich panel of cellular concrete which was fabricated during this research was found to be relatively heavy and non-flammable with an excellent strength of 4.0 MPa. Compared with a light concrete panel, considering the compressive strength that accountsfor 10 MPa, it appeared relatively low in strength. However it would be excellent for application due to the light density of only 0.4 MPa.