Phase Transformation Behavior of Bi2O3-ZnO-Nb2O5 Ceramics sintered at low Temperature

To co-fire with commercial LTCC (Low Temperature Co-fired Ceramic) materials at $850^{\circ}C{\sim}880^{\circ}C$, different contents of $B_2O_3$ were added to the $Bi_2O_3-ZnO-Nb_2O_5$ (BZN) ceramics. According to the test results, the cubic phase of BZN was transformed into orthorhombic in all the test materials. $BiNbO_4$ phase was formed in test materials with $2{\sim}5wt%$ of $B_2O_3$ addition. The phase transformation of cubic BZN was controlled during the synthesis process with excess ZnO content. The Cubic and orthorhombic phases of BZN could coexist and be sintered densely at $850^{\circ}C/2hr$.