Abstract
Main components of metakaolin(MK) were $SiO_2\;and\;Al_2O_3$. and specific surface was 2.2 times larger than that of ordinary portland cement(OPC). MK indicated the fine particle and fiber texture. Flow value of mortar with MK was decreased linearly each $13\%$ as the replacement ratio of MK was increased each $5\%$. Compressive strength of mortar with MK was increased more than that of mortar with OPC by 3days. Compressive strength of mortar with $10\%$ MK was about 83MPa at 28 days. When MK was replaced with $10\%$ of cement volume, flexural strength and modulus of elasticity of mortar was indicated the maximum value at 28 days.