고특성 REBCO 초전도 박막 제조를 위한 새로운 MOD 전구 용액 제조

New MOD solution for the preparation of high $J_c$ REBCO superconducting films

Various organic acid were used in order to prepare new metalorganic deposition solution for high quality $REBa_2Cu_3O_{7-{\delta}}$ (RE=Y, Eu, Gd) films. Prepared fluorine free MO precursor solution was coated on single crystal (001) $LaAlO_3$ (LAO) by dip coating method. Processing parameters such as oxygen partial pressure, water vapor, ramping rate and pyrolysis temperature etc havebeen controlled in order to make high $J_c$ films with a good epitaxial relationship with substrate. 0.5 micron-thick film was obtained by single coating and no crack appeared after calcination. Oxygen partial pressure was varied in the range of $100{\sim}1,000 ppm$ and conversion heat treatment was carried out at the temperature of $725{\sim}765^{\circ}C$. A critical transition temperature $(T_{c0})$ of 90K and a critical transport current density $(J_c)$ of $>0.5MA/cm^2$ (77K and self-field) were demonstrated for the YBCO film on (001) oriented LAO substrates with a thickness of 0.5 micron. $I_c$ was determined by utilizing a transport measurement. SEM and XRD investigations confirmed that films were grown epitaxially onto the LAO single crystal substrate. It is thought that fluorine free new MOD solutionis promising for high quality REBCO films.