RF 스퍼터링법에 의한 SBT 커패시터의 열처리 시간 특성

Annealing Time Properties of SBT Capacitors by RF Sputtering method

The $Sr_{0.7}Bi_{2.6}Ta_2O_9$(SBT) thin films are deposited on Pt-coated electrode($Pt/TiO_2/SiO_2/Si$) using a RF magnetron sputtering method. The ferroelectric properties of SBT capacitors with annealing time were studied. In the SEM images, Bi-layered perovskite phase was crystallized at 10min and grains largely grew with annealing tune. SBT thin films are transformed from initial amorphous phase to the fully formed layer-structured perovskite. During the annealing process at $750^{\circ}C$, we found that an fluorite-like stage is formed after 3min. In the XRD pattern, the SBT thin films after 3min annealing time had (105) orientation. The ferroelectric properties of SBT capacitor with annealing time represent a favorable properties at 60 min. The maximum remanent polarization and the coercive electric field with 60 min are $12.40C/cm^2$ and 30kV/cm, respectively. The leakage current density with 60min is $6.81{\times}10^{-10}A/cm^2$.