Electrical Properties of ZnO Varistors with variation of $Nb_2O_5$

$Nb_2O_5$ 첨가에 따른 바리스터의 전기적 특성

ZnO varistor ceramics which were fabricated with variation of added of 0.01, 0.02, 0.03, 0.05, 0.1mol% $Nb_2O_5$ sintered at $1150^{\circ}C$. In the specimen added 0.05mol% $Nb_2O_5$, sintered density was $5.87g/cm^3$ and electrical properties were superior to any other components. The nonlinear coefficient was 75, and clamping voltage ratio was 1.40. And, endurance surge current in the specimen added 0.05mol% $Nb_2O_5$ was $6500A/cm^2$, and deviation of varistor voltage was -1.7%. As P.C.T and T.C.T environment test were succeed in all specimens, and deviation of varistor voltage in the specimen added 0.3mol% $Nb_2O_5$ was -0.81%. All specimens showed a good leakage current property in the High Temperature Continuous Load Test for 1000hr, at $85^{\circ}C$, and variation rate of the varistor voltage was -1.71%.