A Study on the Low Temperature Impact toughness of Flux Cored Arc Weldmetal in offshore Carbon Steel Process Piping

해양 구조물의 Carbon Steel Process piping용 FC 용접부의 저온 충격인성에 관한 연구

The experimental simulation welds using 3kinds of 70ksi titania based flux-cored consumables were performed on 24 inches 24.6-thick API 5L Gr. B pipe with relatively high current, over 300A and four different Post Weld Heat Treaonent(PWHT) conditions at $625^{circ}C$ were applied to each consumable test coupon. It is well known that, in common welding processes such as Submerged Arc Welding(SAW) or Flux Cored A.c Welding(FCAW), the cooling rates in as-deposited weld bead are normally so ,apid that actual precipitation of microalloy carbonitrides, Nb(C,N) or V(C,N) is not likely to occur in the as-welded weld metal, however, during stress relief or PWHT the operation of precipitation can reduce the impact properties of the weld metal. As results of mechanical testing, it is concluded that PWHT at $625^{circ}C$ is detrimental to weld metal impact toughness of Ti-B type flux- cored (FC) welding consumables regardless of the amount of Nb and V, but two optima were exhibited, one at 800ppm Ti, 75ppm 5 and another 360ppm Ti, 54ppm 5.