Zn Diffusion using by Open-tube Method into n-type $GaAS_{0.60}P_{0.40}$ and the Properties of Electroluminescence

Open-tube 방식을 이용한 n-type $GaAS_{0.60}P_{0.40}$에 Zn 확산과 전계발광 특성

To diffuse Zn at solid-state, the $SiO-2$/ZnO/$SiO_2$ wafers was made by PECVD and RF Sputter. Thicknesses of bottom $SiO_2$ and cap $SiO_2$ was about 500 ${\AA}$ and about 3500 ${\AA}$. Diffusion temperatures were $760^{\circ}C$, $780^{\circ}C$, and $800^{circ}C$, and diffusion times were 1, 2, 3, 4, 5, and 6 hr. LED chips were fabricated by the diffused wafers at Fab. The peak wavelength of all chips showed about 625~650 nm and red color. Main reason for Iv change was by diffusion temperature not diffusion time. The lower temperature was the higher Iv. We thick that these properties is because of the very high diffusion temperature.