초록
($Ba_{0.6-x}Sr_{0.4}Ca_x)TiO_3$ (BSCT) (x=0.10, 0.15, 0.20) powder, prepared by the sol-gel method, were mixed with organic vehicle and the BSCT thick films were fabricated by the screen-printing techniques on alumina substrates using the BSCT paste. The structural and the electrical properties were investigated for various composition ratio and sintering temperature. BSCT thick film thickness, obtained by four printings, was approximately 110 ~ 120 ${\mu}m$. The Curie temperature and dielectric constant at room temperature were decreased with increasing Ca content. The relative dielectric constant, dielectric loss and tunability of the BSCT(50/40/10) specimen, which was sintered at $1420^{\circ}C$ and measured at 1MHz, were about 910, 0.46% and 9.28% at 5kV/cm, respectively.