Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference (한국윤활학회:학술대회논문집)
- 2003.11a
- /
- Pages.355-359
- /
- 2003
Friction and Wear Charateristic of TiAlCrN Coating on Hertz Pressure
Hertz 압력에 따른 TiAlCrN 코팅의 마찰$\cdot$ 마멸특성 및 수명 평가
- Woo Sang-Kyu (Graduate School of Mechanical Engineering, Sungkyunkwan University) ;
-
Lee Young-Ze
(School of Mechanical Engineering, Sungkyunkwan University)
- Published : 2003.11.01
Abstract
In this paper, we investigated the wear lift, wear rate, and its transition on the Hertz pressure. In the experiment, we used TiAlCrN coating deposited by the sputtering technique and ball diameter of 10mm, 7.94mm and 4.76mm for the various Hertz pressure. Ball-on-disk sliding tests wire performed under the unlubricated condition. As the diameter of a ball decreased, the failure load of TiAlCrN coating decreased. However, a good correlation was observed between the wear life and Hertz pressure, and all ball specimens showed the infinite wear life at about 450MPa. In measurement of wear rate, as the diameter of the ball inclosed, the wear transition appeared in bigger load. However, a good correlation was observed between the wear rate and Hertz pressure. The transition appeared in the range from 550MPa to 600MPa at all ball speimens.