초록
ZnO epilayer were synthesized by the pulesd laser deposition(PLD) process on $Al_2O_3$ substrate after irradiating the surface of the ZnO sintered pellet by the ArF(193nm) excimer laser. The substrate temperatures was $400^{\circ}C$. The crystalline structure of epilayer was investigated by the photoluminescence and double crystal X-ray diffraction (DCXD). The carrier density and mobility of ZnO epilayer measured with Hall effect by van der Pauw method are $8.27{\times}10^{16}\;cm^{-3}\;and\;299\;cm^2V{\cdot}s$ at 293 K, respectively. The temperature dependence of the energy band gap of the ZnO obtained from the absorption spectra was well described by the Varshni's relation, $E_g(T)\;=\;3.3973\;eV\;-\;(2.69{\times}10^{-4}\;eV/K)T^2/(T\;+\;463K)$. After the as-grown ZnO epilayer was annealed in Zn atmospheres, oxygen and vaccum the origin of point defects of ZnO atmospheres has been investigated by the photoluminescence(PL) at 10 K. The native defects of $V_{Zn}$, Vo, $Zn_{int}$, and $O_{int}$ obtained by PL measurements were classified as a donors or accepters type.