Corrosion Behavior of Austenitic Alloys in the Molten Salts of $LiCl-Li_2O_2$

$LiCl-Li_2O_2$ 용융염계에서 오스테나이트계 합금의 부식거동

As a part of assessment of the structural material for the molten salt handling system, corrosion behavior of austenitic alloys, Fe-base and Ni-base in the molten salt of $LiCl-Li_2O_2$ was investigated in the range of temperature; 650~$725^{\circ}C$, time; 24- 168h, $Li_2O$; 3wt%, mixed gas; Ar-10%$O_2$. In the molten salt of $LiCl-Li_2O_2$, Ni-base alloys showed higher corrosion resistance than Fe-base alloys. Fe-base alloy with low Fe and high Ni contents exhibited better corrosion resistance. The scales of $Cr_2O_3$, $FeCr_2O_4$ on Fe-base alloys were showed, and $Cr_2O_3$, $NiFe_2O_4$ on Ni-base alloys were also showed.

$LiCl-Li_2O_2$용융염계에서 용융염 취급장치의 구조재료를 위한 평가의 일환으로 오스테나이트 합금인 Fe-base 및 Ni-base 합금의 부식거동을 분위기온도; 650~$725^{\circ}C$, 부식시간: 24~168h, $Li_2O$농도; 3wt%, 혼합가스농도: Ar-10%$O_2$에서 조사하였다. $LiCl-Li_2O_2$ 용융염계에서 Ni-base 합금이 Fe-base 합금보다 높은 내부식성을 나타내었으며, 또한 Fe-base 합금에서 Fe의 함량이 낮고 Ni의 함량이 높은 경우 부식저항성이 증가하였다. 아울러 Fe-base 합금의 부식생성물은 $Cr_2O_3$, $FeCr_2O_4$ Ni-base 합금에서는 $Cr_2O_3$, $NiFe_2O_4$로 나타났다.