Removal Efficiency of Organic Iodide on Silver Ion-Exchanged Zeolite and TEDA-AC at High Temperature Process

고온공정에서 은교환 제올라이트 및 TEDA 첨착활성탄의 유기요오드 제거성능

Removal efficiency of methyl iodide at high temperature process by TEDA-impregnated activated carbon used for radioiodine retention in nuclear facility was experimentally compared with that of silver ion-exchanged synthetic zeolite(AgX), In temperature ranges of$30^{\circ}C$ to $400^{\circ}C$, adsorption capacity of un-impregnated carbon was sharply decreased, but TEDA-impregnated carbon showed similar values of adsorption capacity of AgX even around $100^{\circ}C$. Especially, loading amount of methyl iodide on TEDA carbon up to$250^{\circ}C$ represented higher values compared to un-impregnated carbon. Breakthrough curves of methyl iodide in fixed bed packed with AgX and TEDA-impregnated carbon at high temperature was compared. Removal mechanism of methyl iodide on AgX was proposed, based on analysis of by-product gas generated from adsorption reaction.

원자력시설에서 방사성요오드 제거용으로 사용되는 TEDA 침착활성탄의 고온공정에서의 메틸요오드의 제거성능을 은이온제올라이트(AgX)와 상호 비교하였다. $30^{\circ}C~400^{\circ}C$ 온도범위에서 온도에 따른 메틸요오드의 흡착량 및 탈착후 잔존량을 측정한 결과, 비첨착활성탄의 흡착성능은 온도가 증가함에 따라 급격히 감소하지만 TEDA 침착활성탄의 흡착성능은 $100^{\circ}C$부근에서도 AgX와 거의 유사한 값을 나타내었고, 탈착후 잔존량은 $250^{\circ}C$까지도 비침착활성탄에 비하여 매우 높은 값을 유지하였다. 또한 $100^{\circ}C$ 이상의 고온공정에서 AgX 및 TEDA 침착활성탄을 충전한 고정층 파괴특성을 상호 비교하였으며, 반응 생성기체의 분석으로부터 AgX에 의한 메틸요오드 제거 메커니즘을 제안하였다.