Immobiliztion Experiment of Soil Wastes

토양폐기물 고정화 특성실험

The amount of 4,500 drums of soil waste are temporarily stored in KAERI. In order to develop a technology for safe treatment of the soil waste, a number of tests were performed by applying cement and polymer as solidifier. Immobilization specimens were adequately made by mixing soil waste with cement or polymer Compressive strength and leaching tests were performed in order to see the fulfillment to standard of disposal following the storage. A compressive strength, about 5,300psi was obtained from both solidifiers of cement containing 40% of soil waste and polymer containing 60%. The obtained leaching index was larger than 11, which was satisfied with the relevant standard. It was shown that the integrity of the solidified waste much depends on homogenization in solidifying process and hardness of the specimen. Volume reduction of solidified waste with polymer was better than that of cement by 20%.

한국원자력연구소에서 약 4,500드럼 규모의 토양폐기물을 임시로 보관하고 있다. 이를 안전하게 처리하기 위한 고화기술 개발이 필요함에 따라 시멘트와 폴리머를 선정하여 시험을 수행하였다. 이를 위해 토양폐기물에 시멘트와 폴리머를 적절히 혼합하여 고화시편을 제조하였으며, 저장에 따른 처분기준 만족여부를 평가하기 위하여 압축강도시험과 침출시험을 수행하였다. 폐기물함량이 40%인 시멘트고화체와 65%인 폴리머고화체의 압축강도가 약 5,300psi로서 유사하였으며, 침출지수는 11 이상으로서 모든 시편에서 기준치를 만족하였다. 고화과정의 균질한 혼합여부와 시편의 다짐상태가 고화체의 건전성에 큰 영향을 미치는 것으로 확인되었다. 감용효과는 폴리머고화체가 시멘트고화체에 비해 20% 정도 우수한 것으로 평가되었다.