Property of Thermal Conductivity of Light Weight Panel Core Using Light-Weight Aggregate

인공경량골재를 이용한 경량패널 심재의 열전도 특성

In recent year, it has been investigated on the reduction of mass of structures for the purpose of the larger space and the economy with the industry developing very fast and qualitatively. So the purpose of this study is to investigate the manufacture of light weight concrete panel using the artificial light-weight aggregate as a part of the substitution of foamed styrene and polyurethane because of narrow allocable temperature zone in use. The compressive strength, flexural strength, unit weight, absorption test and thermal conductivity were practised at 3, 7 and 28 days after manufacturing the light-weight concrete lot the panel core: the filling ratio of continuous void was defied as 40%, 50%, and 60% and water-cement rate was 35, 40 and 45%. As a result of this, it was revealed that the mixture derived from filling ration of void of 50% and water-cement ratio 40% were developing the best properties of the others.