EFFECT OF INTERMETALLIC COMPOUND ON MECHANICAL PROPERTIES OF Al-Cu DISSIMILAR BRAZING JOINT

  • Koyama, Ken (Department of Mechanical System Engineering Graduate School of Engineering Hiroshima University) ;
  • Shinozaki, Kenji (Department of Mechanical System Engineering Graduate School of Engineering Hiroshima University) ;
  • Ikeda, Kenji (Department of Mechanical System Engineering Graduate School of Engineering Hiroshima University) ;
  • Kuroki, Hidenori (Department of Mechanical System Engineering Graduate School of Engineering Hiroshima University)
  • 발행 : 2002.10.01

초록

Brazing of Al to Cu using AI-Si-Mg-Bi brazing alloy has been carried out in the vacuum furnace. In the bonded interlayer, there were two kinds of intermetallic compounds. One of these intermetallic compounds was e phase and the other was b phase. The growth of b phase was controlled by diffusion Al into Cu. Deformation behavior of Al-Cu brazing joint was brittle without deformation of the base metal. Shear strength of the joint was only about 20MPa. The shear specimen broken in the intermetallic compound, which was mainly e phase. Shear strength did not depend on the bonding temperature.