Abstract
Polycrystalline Cu(In,Ga)Se$_2$(CIGS) thin-films were grown by co-evaporation on a soda lime glass substrate. In this paper the effects of the Se evaporation temperature on the properties of CuIn0.75Ga0.25Se2 (CIGS) thin films. Structure, surface morphology and optical properties of CIGS thin films deposited at various Se evaporation temperatures have been investigated using a number of analysis techniques. X-ray diffraction (XRD) analysis shows that CIGS films exhibit a strong <112> preferred orientation. As expected, at higher Se evaporation temperatures the films displayed a lower degree of crystallinity. The <112> peak was also enhanced and other CIGS peaks appeared simultaneously. These results were supported by experimental work using scanning electron microscopy When the Se evaporation temperature was increased, the average grain size also decreased together with a reduction Cu content. The Se evaporation temperature also had a significant inf1uence on the transmission spectra. Increasing the Se evaporation temperature, the cell efficiency was improved dramatically to 11.75% with Voc = 556 mV, Jsc = 32.17 mA/cm2 and FF = 0.66. The Se evaporation temperature is an important parameter in thin film deposition regardless of the deposition technique being used to deposit thin films