A Study on the resistance of surface hardening treated Aluminum, Titanium alloy under the high velocity impact

표면 경화 처리된 Al, Ti의 고속 충격 저항성에 관한 연구

  • 손세원 (건국대 기계항공공학부) ;
  • 김희재 (육군사관학교 무기공학과) ;
  • 홍성희 (건국대 대학원 기계설계학과) ;
  • 김영태 (건국대 대학원 기계설계학과)
  • Published : 2002.05.01

Abstract

In order to investigate the fracture behaviors(penetration modes) and resistance to penetration during ballistic impact of surface hardening treated Aluminum, Titanium alloy laminates, ballistic tests were conducted. In this paper, Anodized Al 5083-H131 alloy laminates and nitrified Ti (Gr.2) alloy laminates were used to achieve higher surface hardness. Surface hardness test were conducted using a Micro victor's hardness tester and thickness of surface hardening treated specimens was measured by video microscope. Resistance to penetration is determined by the protection ballistic limit($V_50$), a statistical velocity with 50% probability far complete penetration. Fracture behaviors and ballistic tolerance, described by penetration modes, are respectfully observed at and above ballistic limit velocities, as a result of $V_50$ test and Projectile Through Plates (PTP) test methods. PTP tests were conducted with $0^{\circ}$ obliquity at room temperature using 5.56mm ball projectile. $V_50$ tests with $0^{\circ}$ obliquity at room temperature were conducted with projectiles that were able to achieve near or complete penetration during PTP tests.

Keywords