The Ferroelectric Frequency characteristics of $Bi_{4-x}La_{x}Ti_{3}O_{12}$ ceramics with the variation of Lanthanum additives

La 첨가량에 따른 $Bi_{4-x}La_{x}Ti_{3}O_{12}$ 강유전체의 주파수특성

In recent year, Ferroelectric $BLT(Bi_{4-x}La_{x}Ti_{3}O_{12})$ is a promising candidate materials. This study was practiced to make good conditions of BL T targets. In this study, calcination and sintering temperature were kept at $750^{\circ}C$, $1100^{\circ}C$ for 2 hour respectively. the density obtained 7.612, 7.98, $7.877g/cm^{3}$ as $La_{2}O_{3}$ contents were 0.0mol%, 0.25mol%, 0.5mol%. Especially, the lanthanum content of 0.5 mol% measured C-axis (117) preferred orientation more than the others targets in the XRD. In $\varepsilon_{r}-f$ relationship using by HP 4194 A impedance analyzer, the 0.5 mol% observed above 200 relative dielectric constant. but the dissipation factor was higher than others targets at 100Hz~13MHz range. SEM photograph with the content of $La_{2}O_{3}$ was observed like rod and plate types.